Coke oven

“ Specialized in New Type of Silica Refractories for Glass Furnace & Coke Oven ”

Home>Applications>Coke Oven
Applied to the Front Furnace Wall Repaired with Zero Expansion Silica Bricks

Applied to the Front Furnace Wall Repaired with Zero Expansion Silica Bricks
Applied to the Front Furnace Wall Repaired with Zero Expansion Silica Bricks

Applied to the Front Furnace Wall Repaired with Zero Expansion Silica Bricks
Application of Silica Bricks in Coke Oven

Application of Silica Bricks in Coke Oven
Application of Silica Bricks in Coke Oven

Application of Silica Bricks in Coke Oven
After Repairing Zero Expansion Silica Bricks for Coke Oven Thermal Repair

After Repairing Zero Expansion Silica Bricks for Coke Oven Thermal Repair
After Repairing Zero Expansion Silica Bricks for Coke Oven Thermal Repair

After Repairing Zero Expansion Silica Bricks for Coke Oven Thermal Repair
Silicon Brick Masonry on Coke Oven

Silicon Brick Masonry on Coke Oven
Application of Zero Expansion Silica Brick in Coke Oven Maintenance

Application of Zero Expansion Silica Brick in Coke Oven Maintenance
Application of Ceramic Welding Repair

Application of Ceramic Welding Repair

Recommended products

Fused Silica Brick for Coke Oven

Fused Silica Brick for Coke Oven

SiO2:≧ 99%
Fe2O3:≦0.3%
CaO:≦0.1%
Bulk Density:≧1.85g/cm3
Apparent Porosity:≦18%
:524, 525, 526, 527, 506, 523
Fused Silica Modular Block for Glass Kiln

Fused Silica Modular Block for Glass Kiln

SiO2:≧ 96.6%
Fe2O3:≦2%
CaO:≦1%
Bulk Density:≧1.9g/cm3
Apparent Porosity:≦18%
:530, 531, 533, 532
Fused Silica Modular Block for Coke Oven

Fused Silica Modular Block for Coke Oven

:524, 525, 526, 527, 506, 523
Silica Brick for Coke Oven

Silica Brick for Coke Oven

SiO2:≧ 95%(KN) / 95%(KD) / 95%(KS) / 95%(GMD)
Fe2O3:≤1%(KN) / 1%(KD) / 1%(KS) / 1%(GMD)
CaO:≤3%(KN) / 3%(KD) / 3%(KS) / 3%(GMD)
Bulk Density:≥1.8g/cm3(KN) / 1.84g/cm3(KD) / 1.88g/cm3(KS) / 1.9g/cm3(GMD)
Apparent Porosity:≤24%(KN) / 21%(KD) / 19%(KS) / 15%(GMD)
:524, 525, 526, 527, 506, 523
Ceramic Welding Powder & Projection

Ceramic Welding Powder & Projection

SiO2:≧ 95%
Bulk Density:≧2.0g/cm3
Apparent Porosity:≦17%
TCold Crushing Strength:≧60Mpa
Thermal expansion(1200℃):≦1.25-1.3%
Thermal Conductivity(1000℃):2.13W/m·k